作　　者： ; ; ; ;

机构地区： 厦门大学

出　　处： 《稀有金属材料与工程》 2019年第6期1803-1808,共6页

摘　　要： 利用EPMA技术测定了Ni-Nb-Ti三元系富Ni侧合金在1273K下的扩散数据,并使用Whittle和Green方法计算了Ni-Nb-Ti三元系在1273 K下的互扩散系数。通过DICTRA软件优化得到Ni-Nb-Ti三元系的fcc相的原子迁移率,运用优化得到的的原子迁移率计算出的互扩散系数与实验数据具有较好的一致性,从而验证了所得的原子迁移率的可靠性。同时通过运用原子迁移率拟合各扩散偶的的浓度-距离曲线和扩散路径,进一步验证了原子迁移率的合理性。 Experimental diffusion data in Ni-rich fcc Ni-Nb-Ti alloys at 1273 K was measured by electronic-probe microanalysis and the interdiffusion coefficients have been determined using Whittle and Green method. The atomic mobilities of Ni, Nb and Ti in Ni-Nb-Ti alloys have been obtained through assessing the interdiffusion data critically with the DICTRA software. Comprehensive comparisons between calculated and experimental diffusion coefficients show that the atomic mobilities obtained in this work could well reproduce the experimental data. And the validity of the diffusion mobilities was tested by simulating the concentrationdistance profiles and diffusion paths in diffusion couples.

关 键 词： 合金 原子迁移率 互扩散系数 扩散偶