作 者: (赵景川); (焦宝祥); (刘银); (田浩); (胡聪);
机构地区: School of Materials Science and Engineering, Yancheng Institute of Technology
出 处: 《结构化学》
摘 要: A series of red emitting ZnTiO3 phosphors co-doped with Eu3+ and alkali metal ions(Li+, Na+ and K+) was prepared by sol-gel method. The crystal structure of the phosphors was investigated by using X-ray diffraction(XRD) and transmission electron microscopy(TEM) after annealing at 700 ℃. The results show that the crystal structure belongs to the hexagonal phase of ZnTiO3 with space group R-3:R. The influence of site occupancy of different alkali metal ions on the emission of ZnTiO3:Eu3+ phosphors was investigated in detail. The emission intensity was significantly enhanced by introducing alkali metal ions. In contrast to Eu3+ singly doped ZnTiO3, the red emission intensities of ZnTiO3:Eu3+ with 4 mol% alkali metal ions(Li+, Na+, K+) were enhanced by about 2.1, 1.7 and 1.4 times, respectively. In addition, the Commission Internationale Ed I’eclairage(CIE) chromaticity coordinates of ZnTiO3:Eu3+, Li+(0.672, 0.328) are quite similar to the National Television Standard Committee(NTSC) standard values for the red(0.670, 0.380).
分 类 号: [TQ422]