作　　者： ; ; ;

机构地区： 山东大学材料科学与工程学院材料液态结构及其遗传性教育部重点实验室

出　　处： 《焊接》 2004年第3期13-15,19,共4页

摘　　要： 研究了扩散焊接工艺参数对Fe3Al/18-8扩散界面结合状态、接头组织结构和剪切强度的影响。采用扫描电镜(SEM)分析了不同焊接工艺参数下Fe3Al/18-8扩散焊接头的显微组织特征。结果表明,控制加热温度1 040℃,保温60 min,焊接压力15 MPa时,可以获得组织均匀、强度较高的Fe3Al18-8扩散焊接头。 The effects of diffusion welding technology parameters on the combination of the Fe3Al/18 -8 interface, microstructure and shear strength were studied. The microstructure feature in the diffusion - welded joint of Fe3Al/18 - 8 was observed by means of scanning electron microscope (SEM). The results indicated that by controlling heating temperature 1040 ℃, holding time 60 min and welding pressure 15 MPa,diffusion - welded joint of Fe3 Al/8 - 8 with excellent microstructure performance and high strength could be obtained.

关 键 词： 异种焊接 扩散焊接 剪切强度 显微组织 工艺参数

领　　域： [金属学及工艺]