作　　者： ; ; ; ; ; ;

机构地区： 国防科学技术大学航天与材料工程学院

出　　处： 《火炸药学报》 2003年第1期37-39,46,共4页

摘　　要： 为了研究纳米Bi2O3·SnO2对推进剂燃烧的催化作用,以BiCl3和SnCl4·5H2O为原料,采用共沉淀法制备出纳米Bi2O3·SnO2粉体,产物的粒径约为5nm。用DSC测试了纳米Bi2O3·SnO2对RDX热分解特性的影响。结果表明,纳米Bi2O3·SnO2对RDX热分解有明显的催化效果,使RDX的分解峰温前移了13.7℃,放热量增加665J/g,活化能降低49.42kJ/mol。 Nanocomposite oxide Bi2O3·SnO2 was synthesized by coprecipitation method using BiCl3 and SnCl4·5H2O as the reactant. The particle size, crystal form and phase were determined with XRD and TEM. Average particle size of samples were about 5 nm. The effect of nanocomposite oxide Bi2O3·SnO2 on the thermal decomposition characteristics of RDX was investigated by DSC. The results show that due to the effect of nanocomposite oxide Bi2O3·SnO2, the peak temperature of thermal decomposition of RDX shifts 13.7℃ downward, the decomposite enthalpy ΔH of RDX increases 665 J/g(about 59.9%), and the apparent activation energy of the thermal decomposition of RDX decreases 48.42 kJ/mol.

关 键 词： 纳米氧化铋 氧化锡 制备方法 黑索今 热分解 实验 共沉淀法 推进剂 催化作用

领　　域： [一般工业技术] [航空宇航科学与技术] [航空宇航科学技术]