摘　　要： 研究了CPE、SBS与MMA在甲苯、丁酮混合溶剂中的三元接枝共聚反应,并用红外光谱和扫描电镜对接枝产物进行了表征。结果表明,在SBS接枝体系中引入不超过骨架聚合物(SBS+CPE)总量25%的CPE,可提高所制胶粘剂对PVC人造革的粘合性能。 The ternary graft copolymerization of SBS and CPE with MMA in the mixed solvent of toluene-methylethyl ketone (mass ratio 10∶3) was investigated. IR and SEM were used to characterize the graft polymers. The results showed that the adhesives had high adhesion to PVC artificial leather when the amount of CPE was less than 25% of total amount (SBS+CPE).