作　　者： ; ; ; ; ; ; ;

机构地区： 华南理工大学化学与化工学院

出　　处： 《电镀与涂饰》 2012年第1期55-58,共4页

摘　　要： 以丙烯酸甲酯(MA)、丙烯酸乙酯(EA)、丙烯酸丁酯(BA)、环氧树脂和乳化剂分别制备核、壳预乳化剂,然后通过种子乳液聚合法制备了具有核壳结构的聚合乳液。以环氧树脂E-44和有机硅氧烷KH-570对聚合乳液进行改性,制备了印花涂料用乳液。研究了乳化剂和核壳单体的配比以及不同改性剂用量对乳液稳定性和成膜性能的影响。结果表明,制备乳液的较佳条件为:复合乳化剂[m(十二烷基硫酸钠)∶m(非离子型乳化剂OS-15)=1∶3]的质量分数为4%,核单体组成为m(MA)∶m(EA)∶m(BA)=1∶1∶3、质量分数为30%～40%,壳单体组成为m(MA)∶m(EA)∶m(BA)=2∶1∶1,改性剂环氧树脂E-44和有机硅氧烷KH-570的用量分别为2%和6%。当烘焙工艺条件为140℃/3min时,制得的印花涂料涂膜在弹性、手感、牢度等性能指标方面均达到了设计要求。 Abstract： A core-shell polyemulsion was obtained by seeded emulsion polymerization of a core and a shell pre-emulsifiers synthesized with methyl acrylate （MA）, ethyl acrylate （EA）, butyl acrylate （BA）, epoxy, and emulsifier, and then modified by epoxy resin E-44 and organic siloxane KH-570 to prepare a printing coating. The effects of mass ratios and dosages of emulsifier and core/shell monomers, as well as different modifiers and their dosages on emulsion stability and coating properties were studied. The optimal conditions for preparing the emulsion were determined as follows： mass fraction of the composite emulsifier （composed of sodium dodecyl sulfate and nonionic emulsifier OS-15 at a mass ratio of 1：3） is 4%; the core monomer with a mixture ratio of m （MA） ： rn （EA） ： rn （BA） = 2：1：1 is 30%; the composition of shell monomer is m （MA） ： rn （EA） ： rn （BA） = 2：1：1; and the dosage of modifier is 2% for epoxy resin E-44 and 6% for organic siloxane KH-570. The performance indexes of the printing coating baked at 140℃ for 3 min, meet the design requirement in the aspects of flexibility, hand feeling, and adhesion.

关 键 词： 水性印花涂料 乳液 乳化剂 聚丙烯酸酯 环氧树脂 有机硅氧烷 改性

领　　域： [化学工程]