机构地区： 中南大学材料科学与工程学院

出　　处： 《Transactions of Nonferrous Metals Society of China》 2011年第8期1685-1691,共7页

摘　　要： In order to study the welding process,microstructure and properties of Al-Mg-Mn-Sc-Zr alloy,comparative methods of friction stir welding（FSW） and tungsten inert gas（TIG） were applied to the two conditions of this alloy,namely hot rolled plate and cold rolled-annealed plate.The relationships between microstructures and properties of the welded joints were investigated by means of optical microscopy and transmission electron microscopy.Compared with the base metal,the strength of FSW and TIG welded joints decreased,and the FSW welding coefficients were higher than the TIG welding coefficients.The loss of substructure strengthening and a very little loss of precipitation strengthening of Al3（Sc,Zr） cause the decreased strength of FSW welded joint.But for the TIG welded joint,the disappearance of both the strain hardening and most precipitation strengthening effect of Al3（Sc,Zr） particles contributed to its softening.At the same time,the grains in weld nugget zone of FSW welded joints were finer than those in the molten zone of TIG welded joints. 研究Al-Mg-Mn-Sc-Zr合金的焊接工艺和焊接接头组织和性能。采用搅拌摩擦焊(FSW)和氩弧焊(TIG)2种焊接工艺对该合金的热轧和冷轧-退火2种使用态板材进行焊接。采用比较研究的方法测定和研究焊接接头的力学性能和显微组织,利用光学显微镜和透射电子显微镜研究焊缝的显微组织和力学性能之间的关系。结果表明,与基材相比,Al-Mg-Mn-Sc-Zr合金的热轧和冷轧-退火板材的FSW和TIG焊接接头的强度均下降,但FSW焊接系数高于TIG焊接系数。这是因为FSW焊接接头焊核区亚结构强化的丧失和Al3(Sc,Zr)的析出强化作用的极少量丧失,而TIG焊焊接接头的软化主要原因是其形变强化的完全丧失和Al3(Sc,Zr)的析出强化作用的大部分丧失,且搅拌摩擦焊焊核区晶粒比TIG焊的焊缝区晶粒更细小。

领　　域： [金属学及工艺] [一般工业技术] [金属学及工艺]