作　　者： ; ;

机构地区： 华南理工大学

出　　处： 《铸造技术》 1999年第6期40-42,共3页

摘　　要： 利用Ａｌ２（ＳＯ４）３ 分解反应所制备的多元增强铝基复合材料，其中Ａｌ２Ｏ３ 和ＳｉＣ 颗粒和基体结合良好，分解的ＳＯ３ 对ＳｉＣｐ／ Ａｌ 复合材料熔体进行精炼、除气，试样中没有发现气孔、团聚、集聚、偏析，克服了传统搅拌铸造所带来的铸造缺陷，解决了回收利用重熔过程中的吸气、精炼问题；从而为颗粒增强铝基复合材料走向实用化打下了基础。 In situ Al 2O 3 decomposed from Al 2(SO 4) 3 and SiCp reinforced aluminium matrix composites was fabricated through stirring cast by adding Al 2(SO 4) 3 and SiCp to the molten alloy SO 3 decomposed from Al 2(SO 4) 3 may refine and remove the gas from the molten composites as a result, Al 2O 3,SiCp and matrix bonded well, no cast defects were found,such as gas hole,porosity and particles segregation the composites It provides a basic way of making reinforced aluminium matrix composites in industrial that can make use of SO 3 to refine and remove the gas from the molten composites

关 键 词： 复合材料 铝基 多元增强 碳化硅 氧化铝