热连轧Ti-6Al-4V合金的蠕变行为及影响因素
Creep behaviors and effect factors of hot continuous rolled Ti-6Al-4V alloy

作  者: ; ; ; ; ; ;

机构地区: 沈阳工业大学材料科学与工程学院

出  处: 《中国有色金属学报》 2010年第2期250-256,共7页

摘  要: 采用热处理、蠕变性能测试及位错组态的衍衬分析,研究热连轧Ti-6Al-4V合金的蠕变行为及影响因素。结果表明:经低于β相变点的固溶处理,合金的组织结构由高固溶度的等轴α相和网篮组织组成;随着固溶温度提高,网篮组织数量增多;经1000℃固溶处理后合金可获得完全网篮组织;与940℃固溶时效合金相比,经1000℃固溶时效合金在420℃、575MPa条件下具有较低的应变速率和较长的蠕变寿命;在试验的温度和应力范围内,计算出该合金的蠕变激活能为249.8kJ/mol;在蠕变期间,热连轧合金的变形机制是位错在具HCP结构的α相中发生双取向滑移,940℃固溶处理合金的蠕变机制是波浪状位错在α相中发生锥面滑移,而经1000℃固溶处理合金的变形机制是(1/2)<111>位错在具BCC结构的β相中发生多系滑移;经1000℃固溶处理合金中所含的高含量富V的β相可提高合金蠕变抗力,这是合金具有较低应变速率和较长蠕变寿命的主要原因。 By heat treatment, measurement of creep properties and contract analysis of dislocations configuration, the creep behaviors and the effect factors of hot continuous rolled (HCR) Ti-6Al-4V alloy were investigated. The results show that, after the alloy solution treated at temperatures lower than ,8 phase transformation point, the microstructures of the alloy consist of the supersaturation equiaxial a phase and network basket structure. The quantities of the network basket structure increase as the solution temperature increases, and the full network basket structure may be obtained after solution-treated at 1 000℃. Compared with the alloy solution treated at 940 ℃, the alloy solution treated at 1 000℃ displays a lower strain rate and a longer creep lifetime under the conditions of the applied stress of 575 MPa at 420℃. In the range of the applied temperatures and stresses, the creep activation energy of the alloy is calculated to be 249.8 kJ/mol. The deformed mechanism of HCR alloy during creep is double orientation slipping of dislocations activated within a phase with HCP structure, while the deformed feature of the alloy solution treated at 940℃ is the wave-like (a+c) dislocations activated on the pyramidal planes in a phase. After solution treated at 1 000℃, the deformed mechanism of the alloy is the multiple slipping of (1/2) (111) dislocations activated within,8 phase with BCC structure. In this alloy, the high volume fraction V-riched β phase may enhance the creep resistance of the alloy. This is the main reason why this alloy possesses relatively low strain rate and long creep lifetime.

关 键 词: 合金 热连轧 固溶处理 蠕变 变形机制

领  域: [金属学及工艺] [一般工业技术] [金属学及工艺] [化学工程]

相关作者

作者 林永升
作者 徐涛
作者 曾雪珊
作者 李威
作者 杨城

相关机构对象

机构 暨南大学
机构 华南理工大学
机构 华南师范大学
机构 中山大学
机构 华南理工大学工商管理学院

相关领域作者

作者 刘洋
作者 卢镜
作者 王枫红
作者 张德鹏
作者 邓线平