机构地区： 华南理工大学化学与化工学院

出　　处： 《电镀与涂饰》 2009年第12期49-52,共4页

摘　　要： 采用溶胶–凝胶法,以正硅酸乙酯(TEOS)和甲基三乙氧基硅烷(MTES)为前驱体、硅丙树脂为成膜物质,制备了有机–无机杂化超疏水材料。在对用该材料获得超疏水涂层的研究中,考察了硅丙树脂的含量,比值n(MTES)/n(TEOS)、n(C2H5OH)/n(TEOS)和n(NH3·H2O)/n(TEOS)对涂层性能的影响。测试结果表明,当硅丙树脂加入量占总物料量的25%(质量分数),摩尔比n(TEOS)∶n(MTES)∶n(C2H5OH)∶n(NH3·H2O)为1∶4∶30∶10时,涂层具有良好的疏水性和均匀的外观结构,涂层静态水接触角可达156°。 An organic-inorganic hybrid superhydrophobic coating was prepared by sol-gel method with tetraethoxysilane （TEOS） and methyltriethoxysilane （MTES） as precursors and silicone acrylate resin as film-forming materials. The effects of the content of silicone acrylate resin and the molar ratios of MTES to TEOS, C2H5OH to TEOS and NH3·H2O to TEOS on coating performance were studied. The test results showed that the hybrid coating has good hydrophobicity and uniform appearance. The static state water contact angle is up to 156° when the content of silicone acrylate resin is 25% （mass fraction） and the molar ratio of TEOS ： MTES ： C2H5OH ： NH3·H2O is 1 ： 4 ： 30 ： 10.

关 键 词： 超疏水涂层 溶胶 凝胶法 有机 无机杂化 水接触角