作　　者： ; ;

机构地区： 北京化工大学材料科学与工程学院

出　　处： 《橡胶工业》 1998年第5期259-263,共5页

摘　　要： 考察了共混方法、共混温度、共混时间、共混比等对高聚合度聚氯乙烯（ＨＰＶＣ）／ＮＢＲ共混体系结构与性能的影响。结果表明，采用二阶共混法可获得最佳共混效果，共混温度宜控制为１７５～１８５℃；ＨＰＶＣ／ＮＢＲ共混体系是宏观相容、微观相分离体系，与普通ＰＶＣ／ＮＢＲ共混体系相比。 The influence of the bleding process,temperature,cycle and ratio on the structure and properties of HPVC/EPDM blend was studied.The results showed that the optimal blending effect could be obtained by using onestep process at 170～175 ℃;HPVC/EPDM blend was a thermodynamically incompatible system and 9 phr of CPE or PVCgMAH was suitable interface compatibilizer for the HPVC/EPDM blend with ratio of 30/70;the interface strength of HPVC/EPDM blend could be characterized with Kraus equation.

关 键 词： 高聚合度 聚氯乙烯 共混 橡塑共混 丁腈橡胶

领　　域： [化学工程] [化学工程]