作　　者： ; ; ; ; ; ; ;

机构地区： 北京工业大学材料科学与工程学院

出　　处： 《光散射学报》 2008年第3期200-205,共6页

摘　　要： 采用wolframite前驱物法制备了Pb(Sc1/2Nb1/2)O3陶瓷。通过调节陶瓷烧结工艺,获得了三种具有不同B位离子有序度的PSN陶瓷。测量了三种陶瓷样品在室温至160°C范围内的Raman光谱随温度变化。结果表明,随着温度的升高,三种不同B位有序度的陶瓷样品中,Raman光谱中位于530 cm-1的F2g模的峰位和半峰宽分别在100°C,85°C和80°C发生了突变,表明陶瓷分别在100°C,85°C和80°C三个温度点发生了铁电-顺电相变。上述结论得到了介电温度谱测量数据的支持。 A wolframite precursor method was used to prepare the Pb（Sc1/2Nb1/2）O3 ceramic. Three different Pb（SC1/2Nb1/2）O3 ceramic samples characterized with varied chemical ordering on the B site ions were produced by modifying the annealing treatment. Raman spectra of three different samples are measured from room temperature to 160℃. A ferroelelctric - paraelectric phase transition was observed for three ceramic samples at about 100℃, 85℃ and 80℃, respectively. This conclusion is supported by the dielectric measurement of these ceramic samples.

关 键 词： 陶瓷 铁电相变 有序无序相变 光谱

领　　域： [电气工程] [一般工业技术]