作　　者： ; ; ; ;

机构地区： 长春工业大学化学工程学院

出　　处： 《上海塑料》 2008年第2期1-4,共4页

摘　　要： 要采用乳液聚合方法合成了以丙烯酸丁酯(BA)为橡胶相内核,甲基丙烯酸甲酯(MMA)为壳层,并在壳层接枝甲基丙烯酸环氧丙酯(GMA)的核壳结构聚合物(AcR-g-GMA)。用其增韧聚对苯二甲酸丁二醇酯(PBT),制备PBT/ACR-g-GMA合金。用傅立叶变换红外光谱考察接枝聚合物的环氧基团;用电子显微镜观察共混物中粒子分布的微观形态;测试了共混物的力学性能。结果表明:采用乳液聚舍方法能够将GMA接枝到ACR上,GMA可以增强两相间的界面结合力,ACR-g-GMA粒子能有效地增韧PBT。当ACR-g-GMA粒子中GMA的质量分数为3%,m(PBT)/m(ACR-g-GMA)为80/20时,共混物的缺口冲击强度可高达389 J/m。 Glycidyl methacrylate （GMA） grafted core-shell structured polymer that butyl acrylate as a core and methyl methacrylate as a shell （ACR-g-GMA） is prepared via a multistep seeded emulsion polymerization, which are used to tough PBT resin and prepare PBT/ ACR-g-GMA alloys. Fourier transforms infrared spectroscopic （FTIR） is used to test the epoxy groups in ACR. The morphology of PBT/blends is observed by canning electron microscopy （SEM） , and the mechanical properties are investigated. The results show that GMA can be grafted onto ACR, and GMA can improve the adhesion between PBT and ACR-g-GMA. ACR-g-GMA core-shell impact modifiers are efficient in toughening of PBT. The notched impact strength of PBT/ACR-g-GMA blends is as high as 389 J/m when the mass fraction of GMA is 3% in ACR-g-GMA particles, and m（PBT）/m（ACR-g- GMA） is 80/20.

关 键 词： 核壳结构 丙烯酸酯弹性体 抗冲改性剂

领　　域： [化学工程]