机构地区： 江苏大学材料科学与工程学院

出　　处： 《特种铸造及有色合金》 2008年第2期139-141,共3页

摘　　要： 采用X射线衍射仪(XRD)和扫描电镜(SEM)分析以及力学性能测试,研究了微量Sr对A356-Zr(CO3)2体系熔体反应法合成的(Al2O3+Al3Zr)p/A356复合材料组织及性能的影响。SEM分析结果表明,微量Sr变质后,原位合成的Al3Zr和Al2O3颗粒细小,颗粒尺寸大部分在2～3μm之间;内生Al2O3、Al3Zr颗粒已不被凝固界面大量排斥和推移,而是大部分被捕捉进入固相,均匀分布在基体中;同时Sr使基体A356中Si相形貌从粗针状变为细小的颗粒状。力学性能测试结果表明,Sr变质后的复合材料的抗拉强度比未变质的复合材料提高了13.8%。 Effects of trace Sr on microstructure and mechanical properties of(Al2O3+Al3Zr)p/A356 composites synthesized by the direct melt reaction in A356-Zr(CO3)2 system were investigated by X-ray diffraction(XRD),scanning electron microscope(SEM) and tensile test.SEM observation reveals that in-situ synthesized fine Al3Zr and Al2O3 particles with 2~3 μm in size can be observed,which is uniformly distributed into the matrix due to not be rejected by solid/liquid interface but be engulfed in the solid phase,and the Si phase in the A356 alloy can be converted from coarse acicular into fine particle with trace Sr modification.The tensile strength of the Sr modified composites is increased by 13.8% compared with that of the composites without Sr modification.

关 键 词： 铝基复合材料 微观组织 力学性能 变质

领　　域： [一般工业技术]