摘　　要： 研究了反应性增容对聚丙烯(PP)／纳米SiO2复合材料结晶和流变性能的影响。反应性增容使PP的结晶峰温明显提高,结晶速率增大,球晶细化;复合材料的储能模量、损耗模量和复数黏度明显增大,熔体流动速率减小。在环氧功能化纳米SiO2质量分数为3％,反应性增容剂氨基化PP质量分数为10％时,复合材料的结晶峰温从115.8℃升到125．6℃,熔体流动速率从11．0g/10 min降到8．5 g/10 min。 This paper studied the effect of reactive compatibilization on crystallization and theological behaviors of nano-silica filled polypropylene （PP） composites. The results show that the reactive compatibilization makes PP＇s peak crystallization temperature rise, crystallization rate increase and size dimension of spherulites reduce. The storage modulus, loss modulus and complex viscosity of the composite material remarkably augment, whereas the melt flow index of the PP composites lowers. In the case of adding 3% by mass of surface epoxy functionalized nano-silica and 10% by mass of amine functionalized PP as reactive co the PP composite＇s peak crystallizati mpatibilizer, on temperature ascends from 115.8 ℃ to 125.6 ℃ and melt flow index descends from 11.0 g/10 min to 8.5 g/10 min.

关 键 词： 聚丙烯 纳米二氧化硅 反应性增容 结晶 流变行为

领　　域： [化学工程]