作　　者： ; ;

机构地区： 华南理工大学材料科学与工程学院

出　　处： 《膜科学与技术》 2006年第4期6-9,共4页

摘　　要： 以磺化聚醚醚酮(SPEEK)为基体,以有机改性的蒙脱土(OMMT)为无机相,采用溶液插层法成功制备出了可望应用于直接甲醇燃料电池的SPEEK/OMMT复合型质子交换膜.通过X射线衍射(XRD)表征了复合膜的微观结构,并采用交流阻抗和隔膜扩散方法分别考察了复合膜的质子传导性能和阻醇性能.结果表明,蒙脱土的片层间距超过4.4 nm,SPEEK高分子链已插层到蒙脱土片层之间.与纯SPEEK膜相比,SPEEK/OMMT复合膜的质子传导率有所降低,但在90℃也达到了1.2×10-2S/cm的水平,而且蒙脱土的加入明显地降低了SPEEK膜的甲醇渗透率. Sulfonated poly（ether ether ketone）/organic - montmorillonite （SPEEK/OMMT） composite membranes for application in the direct methanol fuel cell （DMFC） were prepared with SPEEK and OMMT by solution intercalation technique. The microstructure of the composite membranes was characterized by X-ray diffraction （XRD）. The proton conductivity and the methanol permeability were determined by impedance spectrometry and diaphragm diffusion, respectively. The results show that the interlayer spacing of MMT in the S_PEEK matrix exceeds 4.4 nm, the polymer molecule chains of SPEEK have diffused into the MMT gallery. Compared with those of pure SPEEK membrane, the proton conductivity of SPEEK/OMMT composite membrane reduces, however, the conductivity of composite film reaches 1.2×10^-2 S/cm at 90℃. Layers of the OMMT help to reduce the methanol permeability evidently.

关 键 词： 直接甲醇燃料电池 磺化聚醚醚酮 蒙脱土 质子传导率 甲醇渗透率

领　　域： [电气工程]