出　　处： 《粉末冶金工业》 2006年第4期16-20,共5页

摘　　要： 研究了Fe在铜基粉末冶金航空摩擦材料中的摩擦磨损作用及机理。研究表明:Fe在铜基摩擦材料中起到了摩擦组分的作用,对材料的机械性能和摩擦磨损性能起到了重要的作用。Fe能提高铜基摩擦材料的强度、硬度;当Fe含量超过4%后,随Fe含量的增加,材料的摩擦系数及稳定性增加;高速摩擦条件下,Fe能促进摩擦面氧化膜的形成,减小材料的摩擦系数和磨损量。 The working mechanism of Fe in a new type of copper - based P/M friction material was studied. The results show that Fe works as frictional component in copper - based friction materials, influening the mechanical and frictional property of materials. Fe can increase the strength and hardness of friction material; when Fe is more than 4 %, with the increase of Fe, the friction coefficient and stability of the material are enhanced. At the same time, at high speed friction, Fe takes part in formation of oxide film on friction surface, so the wear loss of friction material is decreased.

关 键 词： 粉末冶金摩擦材料 摩擦磨损 摩擦组分 摩擦机理

领　　域： [冶金工程] [冶金工程]