作　　者： ; ;

机构地区： 中南工业大学粉末冶金研究所

出　　处： 《粉末冶金技术》 1996年第3期189-192,共4页

摘　　要： 研究了两种不同成分的陶瓷模材料与ＴｉＡｌ基合金的高温化学相容性。Ｘ射线衍射物相分析结果表明，在１０００℃下，研究的陶瓷模材料与ＴｉＡｌ基合金不发生化学反应，界面上没有形成新的化合物，两者之间有良好的化学相容性。对ＴｉＡｌ基合金试样表面的电子能谱化学成分分析表明，试样表面没有出现陶瓷模材料中的元素。 The chemical compatibility between TiAl hased alloy and ceramiC mold materials at 1000℃has been studied. After heat treated at 1000℃ in air for 2 hours,the interface between TiAl alloy sample and ceramic mold material was analyzed with X-ray diffraction and energy-dispersive analysis of X-ray (EDAX). Except oxides such as TiO2 and A12O3,no other compound was found in the interfsce. Therefore,TiAl alloy showed gial chemical compatibility with ceramic mold materials used in the investigation,and it is practicable to make ceramic mold used in TiAl POwder metallurgical technology from the ceramic mold materials mentioned above.

关 键 词： 陶瓷模材料 化学相容性 钛铝基合金 粉末冶金

领　　域： [冶金工程] [冶金工程]