作　　者： ; ; ; ; ;

机构地区： 上海大学

出　　处： 《核动力工程》 2005年第3期249-253,287,共6页

摘　　要： 将N18锆合金样品分别进行多种变形热处理后,用高分辨透射电镜研究它们的显微组织和第二相粒子,然后把样品放入高压釜,在350℃、16.8MPa、0.01mol·L-1LiOH溶液中进行腐蚀。结果表明:800℃-1h/冷轧/500℃-30h处理的样品,其耐腐蚀性能最好。分析该样品的第二相粒子,发现除了Zr(Fe,Cr)2第二相粒子外,该样品中还存在Nb含量较高的细小的Zr-Nb-Fe第二相粒子;这会降低Nb元素在基体αZr中的固溶含量,提高N18锆合金的耐腐蚀性能。 After being treated in different ways, N18 zirconium alloy specimens are exposed in 0.01 mol·L-1 LiOH aqueous solution at 350°C, 16.8 MPa. The microstructures of these specimens are carried out by high-resolution transmission electron microscopy (HRTEM). The specimen treated by 800°C/C. R/500°C has best corrosion resistance among all the specimens. TEM examination shows, in addition to Zr(Fe, Cr)2, there exist Zr-Nb-Fe SPPs, which containing much more Nb element, in the specimen. The existence of Zr-Nb-Fe SPPs is helpful to the reduction of niobium content in αZr solid solution and results in an improvement in the corrosion resistance of N18 zirconium alloy.

关 键 词： 热处理 耐腐蚀性能 显微组织 第二相粒子

领　　域： [核科学技术]