作　　者： ; ; ; ; ;

机构地区： 华南理工大学化学与化工学院

出　　处： 《涂料工业》 2005年第5期7-10,62,共5页

摘　　要： 考察了聚合工艺、N-羟甲基丙烯酰胺(NMA),甲基丙烯酸二甲氨基乙酯(DMAEMA)、甲基丙烯酸甲酯(MMA)及乳化剂等原材料的用量对印制PVC墙纸用乳液光油及涂膜性能的影响。研究结果表明采用改进型半连续种子乳液聚合工艺能制得粒径为35.6nm,粒径分散性为0.133的乳液,DMAEMA能明显抑制合成含羧酸基和N-羟甲基的聚合物过程中N-羟甲基的自缩聚反应,提高涂膜性能;当ω(NMA)=2%～4%,ω(DMAEMA)=0.5%～1%,ω(MMA)=60%～70%,ω(乳化剂)=2%～4%时制得的罩光油在PVC底材表面具有优异的光泽度、润湿性、附着性以及耐高温热粘性。 This article has reported the influence of the polymerization technology, amount of N-methylol amide (NMA), dimethylamino ethyl methacrylate (DMAEMA), methyl methacrylate (MMA), and emulsifier on the emulsion finish and film for printing PVC wallpaper. It has shown that an emulsion with particle size 35.6 nm and particle size distribution 0.133 can be obtained by use of modified semi-continuous seed emulsion polymerization; DMAEMA will prohibit self polymerization of N-methylol group during preparation of polymer containing carboxyl and N-methylol groups, improving properties of coatings film. When ω(NMA)= 2%～4%,ω(DMAEMA)=0.5%～1%,ω(MMA)=60%～70%,ω(emulsifier)=2%～4%, the clear finish shows high gloss, good wetting, adhesion and heat sticky resistance on PVC substrate.

关 键 词： 丙烯酸酯乳液 甲基丙烯酸二甲氨基乙酯 纸用 印制 羟甲基丙烯酰胺 乳液聚合工艺 墙 涂膜性能 丙烯酸甲酯 研究结果 缩聚反应 原材料 乳化剂 半连续 改进型 分散性 聚合物 光泽度 罩光油 润湿性 耐高温 附着性

领　　域： [化学工程] [化学工程]