机构地区： 浙江大学高分子科学与工程学系高分子科学研究所

出　　处： 《功能材料》 2005年第4期546-548,551,共4页

摘　　要： 通过将聚酰胺酸溶液与硅烷偶联剂处理的钛酸钡(BaTiO3) 粒子进行溶液共混,亚胺化后得到高介电常数的聚酰亚胺/BaTiO3 复合膜。改性后的Ba TiO3 粒子可以均匀地分散在聚酰亚胺基体中, 制备过程中BaTiO3 粒子未发生经晶型改变,而聚酰亚胺分子链的堆积密度有所变化。复合膜的介电常数和介电损耗随着BaTiO3 粒子含量的增加而增加,在50%(体积分数)时,介电常数可达35,介电损耗为0.0082(10kHz),而且在相当大的温度和频率范围内保持稳定,是一种综合性能良好的高介电常数材料。 A series of polyimide/titanate composite (BaTiO3) composite films with high dielectric constant has been successfully prepared by direct mixing poly(amic acid) and silane coupling agent modified BaTiO3 particles followed by imidization. The results showed that silane coupling agent could improve the dispersion of BaTiO3 particles. The dielectric constant (Ε) and the dielectric loss (tgδ) of these composites increased with the increase of the volume fraction of BaTiO3 particles, Ε, tgδ was 35 and 0.0082 respectively at 10 kHz as the composite film containing 50 vol% BaTiO3. Also, the dielectric properties of the composites displayed good stability within a wide range of temperature and frequency.

关 键 词： 聚酰亚胺 钛酸钡 复合膜 介电性能

领　　域： [一般工业技术]