作　　者： ; ; ;

机构地区： 中南大学材料科学与工程学院粉末冶金国家重点实验室

出　　处： 《粉末冶金材料科学与工程》 2004年第3期243-247,共5页

摘　　要： 采用不同球磨介质对Ti+30％HA(质量分数)粉料进行高能球磨,随后在1000℃氩气气氛中热压,研究了球磨工艺对Ti／HA生物复合材料性能的影响。结果表明:随着球磨时间的延长,复合材料的致密度略有下降,硬度上升。热压后,Ti基体形成连通的网络,HA弥散分布于Ti基体中。干磨工艺条件下,球磨时间越长,显微组织越细;湿磨工艺条件下,较短的球磨时间,即可达到较好的细化弥散效果。因此,采用高能球磨,可使Ti／HA生物复合材料在较低的温度下致密化。此外,湿磨介质的存在有利予在短时间内得到力学性能和生物活性较好的Ti／HA生物复合材料。 Ti+30 %HA(mass fraction) composite for biomedical application was obtained by high-energy ball milling and hot-press sinter in Ar at 1 000 ℃. The effect of milling technology on the performances of composite was studied. The results show that increasing the milling time, the density of composite decreases and the hardness increases. After hot press, high density of the composite can be obtained at low temperature, and a continuous network of Ti matrix is formed in which HA disperses. When using dry-milling, the longer the milling time, the finer the network. When using wet-milling, the composite with good mechanical property and bioactivity can be obtained after shorter milling time.

关 键 词： 生物复合材料 球磨工艺 高能球磨 力学性能 生物活性

领　　域： [化学工程] [化学工程]