作　　者： ; ; ; ;

机构地区： 北京工业大学材料科学与工程学院

出　　处： 《中国有色金属学报》 2001年第z1期83-87,共5页

摘　　要： 研究了冷变形对Cu 8～ 13Zn合金室温电阻的影响及其在退火过程中的恢复。结果发现 :相同应变量所导致的电阻增量随Zn含量的增加而增加 ,在大应变量情况下 (断面收缩率为 6 0 %～ 86 % ) ,应变电阻增量与Zn含量基本成正比关系。应变电阻增量的 5 4%在回复退火完成前得到恢复 ,并且恢复量与退火温度成正比关系 。 The influence of cold deformation on the resistivity of Cu 8～13Zn alloys and the resistivity restoring during annealing process were investigated. The results show that the strain resistivity increases with the increases of Zn content for the same cold deformation value. At a large deformation value (section shrinkage up to 60%～85%), the resistivity increment is proportional to Zn content on the whole. 54% of resistivity increment is restored during recovering annealing temperature, and the restoring ratio is proportional to annealing temperature. The rest is restored in the subsequent recrystallization process completely.

关 键 词： 合金 电阻率 热处理

领　　域： [金属学及工艺]